英文题名：A new creep-fatigue crack growth model and a correlation of the creep-fatigue crack growth rate with unified constraint parameter

作者：Lu, Rong-Sheng[1];Tan, Jian-Ping[1];Yang, Jie[2];Wang, Ji[1];Shlyannikov, Valery[3];Wang, Run-Zi[1];Zhang, Xian-Cheng[1];Tu, Shan -Tung[1]

机构：[1]East China Univ Sci & Technol, Sch Mech & Power Engn, Key Lab Pressure Syst & Safety, Minist Educ, Shanghai 200237, Peoples R China;[2]Univ Shanghai Sci & Technol, Sch Energy & Power Engn, Shanghai 200093, Peoples R China;[3]Russian Acad Sci, Inst Power Engn & Adv Technol, FRC Kazan Sci Ctr, Kazan, Russia

年份：2023

卷号：166

外文期刊名：INTERNATIONAL JOURNAL OF FATIGUE

收录：;EI(收录号：20224012823354);WOS:【SCI-EXPANDED(收录号:WOS:000889695100003)】；

基金：This project is sponsored by National Natural Science Foundation of China (52011530036, 51975378) and Shanghai Pujiang Program (Grant No. 21PJD047) .

语种：英文

外文关键词：Creep -fatigue; Crack growth model; Constraint; CFCG rate; Nickel -based superalloys; Finite element model

摘要：Creep-fatigue and constraint are important factors affecting the fracture behavior and service life of components in high-temperature service. Some researchers have attempted to describe creep-fatigue crack growth (CFCG) behavior using constraint parameters. However, there is still no consensus regarding the effect of the constraint on the CFCG rate, and a correlation between the constraint and the CFCG rate must be established. Thus, in this study, a new CFCG model was developed and verified by finite element simulations and experiments. Then, the CFCG behavior for single edge-notched tensile (SENT), centre-cracked tension (CCT), and compact tension (CT) specimens under different constraint conditions was studied using the new model to reveal the effect of constraint on the CFCG rate. The relationship between the dwell time and the CFCG rate was also studied. Moreover, a linear correlation between the CFCG rate and the constraint was established for the first time using the unified constraint parameter Ap, and it is shown that the CFCG rate has a strong correlation with the area surrounded by the equivalent plastic strain (epsilon p) contour at the crack tip. This indicates that the constraint effect on the creep-fatigue could be further revealed by Ap. Furthermore, Ap was extended from monotonic loading to creep-fatigue loading, and a method is provided for using CFCG test data to evaluate high-temperature com-ponents with defects.