中文题名：材料损伤的非线性超声评价研究进展

英文题名：Evaluation of material damage using nonlinear ultrasonic wave

作者：张剑锋[1];轩福贞[1];项延训[1]

机构：[1]华东理工大学机械与动力工程学院,承压系统与安全教育部重点实验室,上海200237

年份：2016

卷号：61

期号：14

起止页码：1536

中文期刊名：科学通报

外文期刊名：Chinese Science Bulletin

收录：CSTPCD;;EI(收录号：20162502515403);北大核心:【北大核心2014】；CSCD:【CSCD2015_2016】；

基金：国家杰出青年科学基金(51325504)资助

语种：中文

中文关键词：非线性超声;材料损伤;无损检测;微观结构

外文关键词：nonlinear ultrasonic wave;material damage;nondestructive test;microstructure

摘要：非线性超声技术由于能够克服传统线性超声的不足,对于微纳尺度缺陷(如位错、微裂纹等)较为敏感,受到研究者的广泛关注.本文介绍了非线性超声技术检测材料损伤的基本原理;对传播过程中非线性超声波与材料微观结构相互作用的理论研究以及非线性超声技术检测、评估材料损伤的实验研究进展进行了综述;最后基于非线性超声损伤检测研究的现状对该技术进一步发展进行了展望.
Generally speaking,damages and defects are inevitable with the operating life consuming of engineer structures.Engineer structures would fail or have to retire ultimately when their load bearing capacity is inadequate to accommodate the working load.It has been revealed that,to ensure the safety and reliability of components,it is essential to accurately evaluate the damages and defects during the service process.Frankly speaking,the traditional linear ultrasonic testing technology is not sensitive to micro-defects being large than 0.2 mm,which usually occur perior to 70%–80%of the material life.By contrast,the nonlinear ultrasonic testing based on the technology of ultrasonic harmonic method provides a possible way for the early evaluation of damages and defects.With the outstanding detective effectiveness and efficiency and high sentivitiy to micro-nano defects,such as dislocations,micro cracks,the nonlinear ultrasonic wave technology has attracted much attention in recent years.In this work,the evaluation of material damages using the nonlinear ultrasonic wave technology was reviewed systematically.Firstly,the basic principle of nonlinear ultrasonic wave technology in the detection of material damages was introduced.One-dimensional longitudinal wave was used as an example to describe how nonlinear ultrasonic wave was generated in damaged solids.Secondly,the interation between the propagating nonlinear ultrasonic wave and microstructures was marked.Three kinds of nonlinear utrasonic wave models were introduced,namely dislocation string models,dislocation dipole models and plastic-dependent models.The advantage and disadvantages of the existing models were discussed comparatively.After that,experimental studies on this topic are presented according to different types of material damage,such as tensile(or compressive)plastic damage,fatigue damage,thermal damage,creep damage,adhesive damage and other damages.Experimental results show that the nonlinear ultrasonic wave technique can characterize the degrees of above damages reasonably accurately.Furthermore,the responses of acoustic nonlinearity depended on the type of damages,materials and loading conditions.Finally,further studies on the evaluation of material damages using nonlinear ultrasonic wave technology were proposed,including the interaciton of nonlinear ultrasonic wave with the discontinuous medium,creation of more robust detective methods and signal processing methods,etc.