中文题名：α/β复合成核剂成核聚丙烯的结晶形态及非等温结晶动力学研究

英文题名：Crystallization Morphologies and Non-Isothermal Crystallization Kinetics of Isotactic Polypropylene Nucleated with α/β Compound Nucleating Agents

作者：石尧麒[1];辛忠[1];赵世成[1]

机构：[1]华东理工大学化学工程联合国家重点实验室化工学院产品工程系,上海200237

年份：2013

卷号：42

期号：11

起止页码：1235

中文期刊名：石油化工

外文期刊名：Petrochemical Technology

收录：CSTPCD;;Scopus;北大核心:【北大核心2011】；CSCD:【CSCD_E2013_2014】；

基金：国家自然科学基金资助项目(U1162110,21306047);中央高校基础研究基金项目(WA1314051,WA1013012);上海市优秀学科带头人计划项目(XD1401500);中国博士后科学基金面上资助项目(2013M541489)

语种：中文

中文关键词：等规聚丙烯;山梨醇;α;β复合成核剂;结晶形态;非等温结晶动力学

外文关键词：isotactic polypropylene; sobitol; α/β compound nucleating agent; crystallizationmorphology; non-isothermal crystallization kinetics

摘要：以山梨醇类S20成核剂为α成核剂与HHPA-Ba和PA-03两种β成核剂分别复配得到α/β复合成核剂.利用DSC和偏光显微镜考察了该复合成核剂对成核等规聚丙烯（iPP）结晶形态的影响,并采用Cazé法研究了成核iPP的非等温结晶动力学.实验结果表明,复合成核剂可减小成核iPP的球晶尺寸,成核iPP最终的结晶形态由复合成核剂中两种成核剂的含量决定.不同配比的复合成核剂均可提高iPP的结晶温度、缩短iPP的结晶时间、提高iPP的成型速率.成核iPP的Avrami指数在4～5之间,最佳配比的S20/HHPA-Ba复合成核剂（S20成核剂的含量为40％（w））成核的iPP以混合成核模式结晶.以S20为α成核剂的α/β复合成核剂对成核iPP的结晶行为和结晶形态的影响基本一致.
α/β Compound nucleating agents（NAs）, S20/HHPA-Ba and S20/PA-03, were prepared by compositing sobitol S20 as α NA and HHPA-Ba or PA-03 as β NA. The effects of the NAs on the crystallization morphologies of the nucleated isotactic polypropylene（iPP） were studied by means of DSC and polarizing microscope, and the non-isothermal crystallization kinetics of the nucleated iPP was investigated by means of Caze method. The results showed that the crystal size of the nucleated iPP appeared much smaller than that of iPP without nucleating agents and its crystallization morphologies depended on the ratio of NA to β NA. Using the compound NAs can raise the crystallization temperature of iPP and shorten its crystallization time. The Avrami exponents of the nucleated iPP are in the range of 4-5. The iPP nucleated with α/β compound NA with the optimum compound ratio crystallized in a mixed mode. The effects of the α/β compound NAs on the crystal morphologies and behaviors of iPP are accordant.