文献类型：期刊文献

英文题名：Evaluation of the catalytic effect and migration behavior of potassium in the molten slag during the char/molten slag interfacial gasification

作者：Bao, Xiaodan[1];Shen, Zhongjie[1];Zhang, Haigang[1];Liang, Qinfeng[1];Liu, Haifeng[1]

机构：[1]East China Univ Sci & Technol, Shanghai Engn Res Ctr Coal Gasificat, POB 272, Shanghai 200237, Peoples R China

年份：2022

卷号：307

外文期刊名：FUEL

收录：;EI(收录号：20213610860678);WOS:【SCI-EXPANDED(收录号:WOS:000709529200007)】；

基金：This study was supported by the National Natural Science Foundation of China (Grant No. 21908063).

语种：英文

外文关键词：Coal gasification; Alkali metal (K); Molten slag; Catalytic effect; Migration behavior

摘要：The reaction of coal char particles deposited on the molten slag surface in the entrained flow gasifier was of importance to the carbon conversion and slag discharge. In this study, the catalytic effect and migration behavior of the alkali metal (K) in molten slag during the gasification reaction of char particles on the molten slag surface were investigated and evaluated by using visualization and surface analytical techniques. The results showed the ionic K in the molten slag was not deactivated and accelerated the char gasification rate and carbon conversion of char particle on the molten slag surface as a catalytic effect. The complete conversion time of char particles on the molten slag with the addition of K was reduced by about 37%-67%, compared to the time of the char gasification without molten slag or the gasification on the slag with no addition of K. The carbon conversion of char particles was increased obviously with increasing the addition of K in the molten slag. From the analyses of scanning electron microscope (SEM) and energy dispersive spectrometry (EDS), the ionic K was found to gradually migrate and accumulate to the interface between the coal char particle and molten slag during the gasification process. The migrating and accumulating amount of K to the interface increased with the increases of both carbon conversion of the char particle and K addition of the slag. With a comparative experiment of the char combustion on the slag surface, a low temperature zone below the char particle during the gasification was key to cause a migration behavior of K with other elements (e.g. Si and Al) and further acted as a catalytic effect on the gasification reaction. Finally, a mechanism of the catalytic effect and migration behavior of ionic K in the slag during the char/molten slag interfacial gasification process was uncovered in this study.