英文题名：Preparation of poly (n-butyl acrylates) encapsulated carbon black via ultrasonic irradiation initiating emulsion polymerization

作者：Li, Qiuying[1]; Wu, Guozhang[1]; Zhang, Xiliang[1]; Wu, Chifei[1]

机构：[1] Polymer Alloy Lab., School of Material Science and Engineering, East China University of Science and Technology, 130 Meilong Road, Shanghai, China

年份：2006

卷号：38

期号：12

起止页码：1245

外文期刊名：Polymer Journal

收录：EI(收录号：20070710422917)

语种：英文

外文关键词：Agglomeration - Carbon black - Emulsion polymerization - Irradiation - Particle size analysis - Reaction kinetics - Surface properties - Synthesis (chemical)

摘要：The encapsulation of poly (n-butyl acrylates) (PBA) onto carbon black (CB) surface via ultrasonic irradiation initiating emulsion polymerization was investigated. The results showed that the route performed at ambient temperature can efficiently prepare PBA encapsulated CB as proved by the aggregation of PBA encapsulated CB in the precipitator of PBA. The surface properties of CB coated with PBA were analyzed by FT-IR and XPS. The content of PBA encapsulated on the CB surface reaches 11.87% determined by TGA. Compared with the conventional chemical modification of CB, it was found that the particle size of CB obtained by the present approach can be controlled, and dynamic light scattering results quantified that CB particles with narrower size distribution and smaller size were obtained, The PBA encapsulated CB can be dispersed uniformly in the polymer matrix. ? 2006 The Society of Polymer Science, Japan.