中文题名：还原剂浓度对原位沉积铂纳米线催化层结构和性能的影响

英文题名：Effects of reducing agent concentrations on structure and properties of in-situ deposited platinum nanowires catalytic layer

作者：曹晓兰[1];隋升[2];李冰[1]

机构：[1]华东理工大学机械与动力工程学院,上海200237;[2]上海交通大学燃料电池研究所,上海200240

年份：2020

卷号：30

期号：3

起止页码：604

中文期刊名：中国有色金属学报

外文期刊名：The Chinese Journal of Nonferrous Metals

收录：CSTPCD;;EI(收录号：20202108679733);Scopus;北大核心:【北大核心2017】；CSCD:【CSCD2019_2020】；

基金：国家自然科学基金资助项目(21576164)。

语种：中文

中文关键词：铂纳米线;原位沉积;还原剂浓度;质子交换膜燃料电池

外文关键词：Pt nanowires;in-situ deposition;reducing agent concentration;proton exchange membrane fuel cell(PEMFC)

摘要：采用湿化学法研究还原剂甲酸浓度对铂纳米线(Pt-NWs)长度和分布的影响以及Pt-NWs对单电池的电化学性能和耐久性的影响。结果表明:随着还原剂浓度的增加(0.075~0.590 mol/L),Pt-NWs的长度先增加后减小,在碳基体层厚度方向上Pt分布从均匀到逐渐聚集在表层,呈现明显梯度特征。当还原剂浓度为0.372 mol/L时,可获得在整个碳基体层厚度方向上分布的Pt-NWs团簇,与商用的催化剂(JMPt/C)相比,在0.6V时,电流密度提高11.3%,最大功率密度提高12.5%,这主要归于Pt-NWs的一维结构、在催化层中的梯度分布以及高Pt利用率。通过加速耐久性测试,Pt-NWs/C的最大功率密度和电化学活性表面积比JM Pt/C的衰减缓慢,说明Pt-NWs/C具有更好的稳定性。
The effects of reducing agent formic acid concentrations on the length and distribution of platinum nanowires(Pt-NWs)and the electrochemical performance and durability of single cells were investigated.The results show that,with the increase of reducing agent concentration(0.075-0.590 mol/L),the length of Pt-NWs increases firstly and then decreases,meanwhile,the distribution of Pt-NWs through thickness direction of the carbon-based layer is from uniform distribution to obvious gradient distribution with gradual aggregation.The Pt-NWs clusters uniformly distribute on the carbon surface are obtained at a reducing agent concentration of 0.372 mol/L.Compared with JM Pt/C,the current density of the Pt-NWs clusters used as the cathode of PEMFC increases by 11.3%at 0.6 V and the maximum power density increases by 12.5%.The improvement of the performance of the Pt-NWs catalytic layer is mainly attributed to the one-dimensional structure of Pt-NWs,the gradient distribution in the catalytic layer,and the high Pt utilization.By 5000 cycles accelerating durability test,the performance degradation of Pt-NWs/C is slower than that of JM Pt/C,indicating its better stability than that of the later.The optimized platinum nanowire catalytic layer obtained promotes the design of novel nanostructures in practical applications.