英文题名：The effects of blue dyes on the properties and crystallization behavior of DMDBS-nucleated isotactic polypropylene

作者：Wang, Yanshu[1];Yu, Chao[2];Liu, Xiuming[2];Jin, Zhilan[1];Li, Jingwen[1];Zhao, Shicheng[1]

机构：[1]East China Univ Sci & Technol, Sch Chem Engn, Shanghai Key Lab Multiphase Mat Chem Engn, Shanghai 200237, Peoples R China;[2]CNOOC Inst Chem & Adv Mat, Beijing 102200, Peoples R China

年份：2026

卷号：33

期号：3

外文期刊名：JOURNAL OF POLYMER RESEARCH

收录：;EI(收录号：20261320335973);WOS:【SCI-EXPANDED(收录号:WOS:001714579200001)】；

基金：The authors gratefully acknowledge the financial support of this work by National Natural Science Foundation of China (Grants 21878089).

语种：英文

外文关键词：Isotactic polypropylene (iPP); DMDBS; Blue dye; Yellowness index; Crystallization behavior

摘要：The nucleating agent 1,3:2,4-Bis(3,4-dimethylbenzylidene) sorbitol (DMDBS) improves the transparency of polypropylene (PP) but often induces yellowing. In this study, a complementary color strategy was employed by incorporating trace amounts of commercial blue dyes, including Acid Blue 74, Pigment Blue 15, and Pigment Blue 29, into DMDBS-nucleated isotactic polypropylene (iPP). Their effects on optical properties, mechanical properties and crystallization behavior were investigated. In terms of optical properties, all dyes effectively reduced the yellowness index (YI). Pigment Blue 15 exhibited the strongest effect by fully counteracting yellowing induced by DMDBS at only 5 & times; 10(- 5) wt%. Meanwhile, the dyes acted synergistically with DMDBS to reduce haze. Pigment Blue 15 and Pigment Blue 29 decreased haze from 32.3% to 21.3%. Regarding mechanical properties, Pigment Blue 29 showed the most pronounced synergistic effect with DMDBS, increasing the flexural modulus by 8.6%. Differential scanning calorimetry (DSC) and polarized optical microscopy (POM) results indicated that all blue dyes promoted the crystallization of DMDBS-nucleated iPP. Pigment Blue 15 exhibited the best performance, increasing the crystallization temperature by approximately 4 degrees C, and accelerating crystallization rates. Finally, analysis of the Avrami exponents (n) of iPP and nucleated iPP showed that the addition of dyes did not change the crystallization growth patterns of the nucleated iPP. This study provides a simple and efficient strategy to counteract the yellowing induced by DMDBS and enhance the transparency of the iPP, which shows great potential for industrial production.