文献类型：期刊文献

中文题名：泡孔结构形貌对环氧树脂发泡材料抗压性能的影响

英文题名：Effect of Cell Morphologies on Compressive Properties of Epoxy Resin Foam

作者：胡冬冬[1];吕佳逊[1];刘涛[1];许志美[1];郎美东[2];赵玲[1]

机构：[1]华东理工大学化学工程联合国家重点实验室,上海200237;[2]华东理工大学材料科学与工程学院,上海200237

年份：2018

卷号：34

期号：7

起止页码：60

中文期刊名：高分子材料科学与工程

外文期刊名：Polymer Materials Science & Engineering

收录：CSTPCD;;EI(收录号：20184305970782);Scopus;北大核心:【北大核心2017】；CSCD:【CSCD2017_2018】；

基金：国家重点研发计划项目(2016YFB0302201);国家自然科学基金面上项目(21676092);中央高校基本科研业务费(222201714005)

语种：中文

中文关键词：环氧树脂;发泡材料;泡孔形貌;抗压性能

外文关键词：epoxy resin;foam;cell morphology;compressive property

摘要：采用超临界CO_2发泡制备了不同泡孔结构和形貌的环氧树脂发泡材料,通过万能材料实验机研究了其抗压性能。采用差示扫描量热分析考察了环氧树脂的固化程度;利用扫描电镜结合排水法密度测试,表征了泡孔形貌、泡孔尺寸、发泡密度及泡孔分布;研究了上述因素对发泡材料抗压性能的影响。结果表明,环氧树脂发泡样品的抗压性能随固化度的增大而增强;当样品完全固化时,闭孔环氧树脂发泡材料的抗压性能较开孔结构和破裂结构强,这与作为支撑结构的泡孔壁的形貌相关。对于闭孔结构的发泡材料,其抗压性能受泡孔尺寸的影响显著,泡孔尺寸越小,材料密度越大,其抗压性能越好。具有双峰泡孔分布的发泡材料,其抗压性能得以改善,较小的泡孔为发泡材料提供了更为致密的支撑骨架结构,比具有同样密度的大尺寸泡孔发泡材料的压缩性能更高。
Epoxy resin foams with different cell structures and morphologies were prepared by supercritical CO2 foaming. The compressive property of the foams,curing degree of epoxy resin,cell morphology,cell size,foam density and cell distribution were studied by mechanical testing machine,DSC and SEM combined with the displacement method.Meanwhile,the effects of epoxy resin curing degree,cell morphology,cell size,foam density and cell distribution on the compressive properties of epoxy resin foams with different cell morphologies were investigated. The results show that the compressive strength increases with curing degree. At a certain curing degree of 100%,the compressive property of closed-cells structure is higher than that of open-cells ones,while that of the cracked foams is the worst. The compressive properties of closed-cells are affected by foam density and cell size,cell size influences the mechanical property significantly. Samples with higher densities,smaller and more cells possess higher compressive strength and modulus. The smaller cell provides better compressive properties in the bimodal structure,exhibiting better compressive properties than the unimodal foaming materials.