文献类型：期刊文献

英文题名：PHASE-SEPARATION IN DEUTERATED POLYCARBONATE POLY(METHYLMETHACRYLATE) BLEND NEAR GLASS-TRANSITION TEMPERATURE

作者：MOTOWOKA, M; JINNAI, H; HASHIMOTO, T; QIU, Y; HAN, CC

机构：[1]NATL INST STAND & TECHNOL,DIV POLYMERS,GAITHERSBURG,MD 20899;[2]MITSUI PETROCHEM IND CO LTD,POLYMERS LAB,YAMAGUCHI 740,JAPAN;[3]E CHINA UNIV CHEM TECHNOL,DEPT POLYMER SCI & ENGN,SHANGHAI 200237,PEOPLES R CHINA

年份：1993

卷号：99

期号：3

起止页码：2095

外文期刊名：JOURNAL OF CHEMICAL PHYSICS

收录：;WOS:【SCI-EXPANDED(收录号:WOS:A1993LN78200071)】；

语种：英文

摘要：Early stage of spinodal decomposition kinetics of deuterated polycarbonate/poly(methylmethacrylate) blend has been studied by the time resolved small angle neutron scattering measurements. A trapped miscible state was obtained through fast solution casting of film specimens. Time dependence of the structure factor, S(q,t), was measured after the specimen temperature was quickly increased to a final temperature which is above its glass transition temperature, T(g). Thus, the early stage of spinodal decomposition kinetics has been observed starting from the dimension (q-1) comparable to the single chain radius of gyration, R(g), for a binary polymer mixture. The results provide an unequivocal quantitative measure of the virtual structure factor, S(q, infinity); the relationship of q(m) and q(c) through rate of growth, Cahn-plot analysis, and singularity in S(q, infinity); the growth of fluctuation of qR(g) < 1 and intrachain relaxation of qR(g) > 1; and also a clear proof of the Cahn-Hillard-Cook theory in the early stage of spinodal decomposition of a mean-field system.