英文题名：Preparation, hydrogen bonding and properties of polyurethane elastomers with 1,2,3-triazoleunits by click chemistry

作者：Gu, Xiao[1];Guo, Shiqing[1];Wang, Guiyou[1]

机构：[1]East China Univ Sci & Technol, Sch Mat Sci & Engn, Shanghai Key Lab Adv Polymer Mat, Shanghai 200237, Peoples R China

年份：2020

卷号：60

期号：12

起止页码：3270

外文期刊名：POLYMER ENGINEERING AND SCIENCE

收录：;EI(收录号：20204209339518);WOS:【SCI-EXPANDED(收录号:WOS:000579112500001)】；

基金：Shanghai Automobile Industry Science and Technology Development Foundation, Grant/Award Number: 0711

语种：英文

外文关键词：elastomers; mechanical properties; morphology; polyurethanes

摘要：Two kinds of diols containing 1,2,3-triazole units were synthesized through the azide-alkyne cycloaddition reaction between propargyl alcohol and 1,4-diazidobutane. One of the diols, (butane-1,4/1,5-diylbis[1H-1,2,3-triazole-1,4/1,5-diyl])dimethanol (BDTDO-1), containing 1,4/1,5-disubstituted 1,2,3-triazole regioisomers, was directly prepared under thermal condition without Cu(I) catalyst. The other diol, (butane-1,4-diylbis[1H-1,2,3-triazole-1,4-diyl])dimethanol (BDTDO-2), containing 1,4-disubstituted 1,2,3-triazoles, was prepared by Cu(I) catalyzed click chemistry. Then, two kinds of 1,2,3-triazole modified polyurethane elastomers (PUEs) were prepared from the reaction of 4,4 '-methylenebis(phenyl isocyanate) and poly(tetramethylene ether) glycol, with BDTDO-1 or BDTDO-2 as the chain extender (CE). It was found that the introduction of 1,2,3-triazoles and their substitution positions had significant influences on the hydrogen bonding, thermal and mechanical properties of PUEs. Compared with the PUE prepared from 1,4-butanediol as the CE, the PUE containing symmetric 1,4-disubstituted 1,2,3-triazoles units in the main chains shows higher values of hydrogen bonding, physical crosslinking density, Young's modulus, tensile strength and melting temperature, while lower glass transition temperature, resulting from the rigid structure and the ability to form more hydrogen bonds. However, the introduction of asymmetric 1,4/1,5-disubstituted 1,2,3-triazole moieties decreases the values of hydrogen bonding, thermal and mechanical properties of PUE appreciably due to the destruction of the ordered structure of the hard segments.