英文题名：Phase and shape controlling of MnS nanocrystals in the solvothermal process

作者：Mu, Jin[1]; Gu, Zhenfang[1]; Wang, Lei[1]; Zhang, Zhiqing[1]; Sun, Hua[1]; Kang, Shi-Zhao[1]

机构：[1]E China Univ Sci & Technol, Dept Chem, Shanghai, Peoples R China

年份：2008

卷号：10

期号：1

起止页码：197

外文期刊名：JOURNAL OF NANOPARTICLE RESEARCH

收录：;EI(收录号：20074810954822);WOS:【SCI-EXPANDED(收录号:WOS:000251152800021)】；

语种：英文

外文关键词：MnS; nanocrystals; solvothermal synthesis; phase; shape; colloids; wet process

摘要：MnS nanocrystals with different phases and shapes were prepared through solvothermal synthesis. The products were characterized by X-ray diffraction (XRD), transmission electron microscope (TEM), UV-vis absorption and photoluminescence (PL) spectra. The solvent and reaction time played an important role in controlling the phase and shape of MnS nanocrystals. The possible mechanism of the shape evolution was investigated, which revealed that the crystal growth along the unique c axis of gamma-MnS resulted in the rod-like MnS at the primary period, and the tetrahedral crystal seed of beta-MnS with zincblende structure resulted in the interlinking of MnS rods, so the zigzag and three-branched and palm-like MnS appeared; with increasing reactive time the thermodynamically stable spherical alpha-MnS was favored through the Ostwald ripening process. The PL results showed that the intensity of gamma-MnS was much weaker than that of alpha-MnS, and the trap state emissions of gamma-MnS at 470 and 482 nm, respectively, disappeared, which might be ascribed to the difference of the shapes between the sphere and the rod or branch.