英文题名：Novel high-flux thin film composite nanofiltration membranes fabricated by the NaCIO pre-oxidation of the mixed diamine monomers of PIP and BHTTM in the aqueous phase solution

作者：Tang, Yong-Jian[1];Wang, Lan-Jie[1];Xu, Zhen-Liang[1];Wei, Yong-Min[1];Yang, Hu[1]

机构：[1]E China Univ Sci & Technol, Membrane Sci & Engn R&D Lab, Chem Engn Res Ctr, State Key Lab Chem Engn, 130 Meilong Rd, Shanghai 200237, Peoples R China

年份：2016

卷号：502

起止页码：106

外文期刊名：JOURNAL OF MEMBRANE SCIENCE

收录：;WOS:【SCI-EXPANDED(收录号:WOS:000368631400012)】；

基金：The authors are thankful for the financial support received from 2013 Special Project of the Development and Industrialization of New Materials of National Development and Reform Commission in China (20132548), the National Science and Technology Support Project of China (2014BAB07B01 and 2015BAB09B01), the Key Technology R&D Program of Shanghai Committee of Science and Technology in China (13521102000) and the Key Technology R&D Program of Jiangsu Committee of Science and Technology in China (BE2013031).

语种：英文

外文关键词：Nanofiltration membrane; Thin film composite membrane; PIP and BHTTM; Interfacial polymerization; Chlorine tolerant

摘要：Novel high-flux thin film composite (TFC) nanofiltration (NF) membranes were fabricated by the sodium hypochlorite (NaCIO) pre-oxidation of the mixed diamine monomers of piperazine (PIP) and 2,2'-bis (1-hydroxyl-1-trifluoromethyl-2,2,2-triflutoethyl)-4,4'-methylenedianiline (BHTTM) in the aqueous phase solution, and via interfacial polymerization (IP) with trimesoyl chloride (TMC) on the polysulfone (PSF) ultrafiltration (UF) membrane. The chemical change of the pre-oxidation aqueous phase solution was characterized by LC-MS. By optimizing the NaCIO and NaOH content in the aqueous phase solution, the pure water flux was improved greatly and the salt rejection kept on a high level ( > 90%). The properties of NF membranes were characterized by XPS, SEM, AFM and contact angle. Through the NaCIO pre-oxidation of the mixed diamine monomers of PIP and BHTTM in the aqueous phase solution, the active layer of NF membrane became thinner and the pore size of NF membrane was enlarged. Besides, after oxidation treatment by 3000 ppm active chlorine solution for 1 h, the NF membrane exhibited pure water flux (PWF) with 161 (LMH) and Na2SO4 rejection of 92.1% under 0.6 MPa. The molecular weight cut-off (MWCO) of the NF membrane was greater than 500, which was calculated from the carbohydrates rejection. The good performance and the satisfactory stability of the novel high-flux NF membrane demonstrated its good potential in the practical application. (C) 2015 Elsevier B.V. All rights reserved.