中文题名：预处理对Ni-Co双金属沼气重整催化剂性能与结构的影响(英文)

英文题名：Effects of pretreatment on performance and structure of Ni-Co bimetallic catalyst for biogas reforming to hydrogen

作者：赵健[1,2];周伟[2,3];马建新[1,2,3]

机构：[1]华东理工大学资源与环境工程学院,上海200237;[2]同济大学新能源汽车工程中心,上海201804;[3]同济大学汽车学院,上海201804

年份：2013

卷号：34

期号：10

起止页码：1826

中文期刊名：催化学报

外文期刊名：CHINESE JOURNAL OF CATALYSIS

收录：;EI(收录号：20134516942540);WOS:【SCI-EXPANDED(收录号:WOS:000325601000005)】；北大核心:【北大核心2011】；CSCD:【CSCD2013_2014】；

基金：This work was supported by the Ministry of Science and Technology International Cooperation Program (2010DFA64080) and the National High Technology Research and Development Program of China (863 Program, 2011AA11A275).

语种：中文

中文关键词：预处理;镍钴催化剂;沼气重整;抗积碳性能;制氢

外文关键词：Pretreatment;Nickel-cobalt catalyst;Biogas reforming;Carbon formation resistance;Hydrogen production

摘要：采用过量浸渍法制备了Ni-Co/La2O3-γ-Al2O3双金属催化剂,并使用固定床石英反应器在850oC,0.1 MPa和空速为6000mL gcat1h 1的条件下考察了预处理对催化剂性能的影响.运用X射线衍射、热重-差示扫描量热、透射电子显微镜、扫描电镜和X射线能谱分析等手段对催化剂进行了表征.结果表明,与传统氢气还原预处理相比,经氢气和二氧化碳预处理后,催化剂性能明显提高,且能基本消除该催化剂上沼气重整反应的诱导期.511 h的稳定性实验结果表明,催化剂经氢气和二氧化碳预处理后具有很好的稳定性和抗积碳性,平均积碳速率仅为0.2 mg gcat1h 1.表征结果显示,经氢气和二氧化碳预处理后,催化剂具有更好的抗烧结和抗积碳性能,反应后金属颗粒较小,分布较均匀,粒径分布范围较窄,从而增强了催化剂的稳定性.
Ni-Co bimetallic catalysts supported on -Al2 O3 pellets for biogas reforming to hydrogen were successfully prepared using the excessive impregnation method.The effects of pretreatment on the catalytic performance were investigated in a fixed-bed vertical quartz reactor under conditions of 850℃,0.1 MPa,and a gas hourly space velocity of 6000 mL gcat 1 h 1(4 g of catalyst,2.5–3.5 mm). The samples were characterized using X-ray diffraction,transmission electron microscopy,thermogravimetry coupled to differential scanning calorimetry, and emission scanning electron microscopy with energy-dispersive X-ray spectroscopy.The results showed that the catalyst pretreated with both H2 and CO2 showed higher activity,and basically eliminated the long induction period of the biogas reforming reaction,compared with the catalyst pretreated with only H2.In a 511 h stability test,the catalyst pretreated with both H2 and CO2 exhibited excellent stability,with a very low carbon deposition rate,ca.0.2 mg gcat–1 h–1.The average conversion of CH4 and CO2,selectivity for H2 and CO,and ratio of H2/CO were 96%,97%,98%,99%,and 0.98,respectively.The characterization results showed that the catalyst pretreated with both H2 and CO2 exhibited higher carbon formation resistance and better anti-sintering performance during reactions;this resulted in smaller metal particles and thus enhanced the stability of the catalyst.This new pretreatment route is very promising for enhancing the performance of biogas reforming catalysts.