文献类型：期刊文献

中文题名：聚己内酯/介孔二氧化硅杂化材料的制备及表征

英文题名：Synthesis and Characterization of Poly(caprolactone)/ Mesoporous Silica Hybrid Materials

作者：王召君[1];刘鹏飞[1];贾丽洲[1];张琰[1];郎美东[1]

机构：[1]华东理工大学材料科学与工程学院,超细材料制备与应用教育部重点实验室,上海市先进聚合物材料重点实验室,上海200237

年份：2013

卷号：39

期号：5

起止页码：542

中文期刊名：华东理工大学学报（自然科学版）

外文期刊名：Journal of East China University of Science and Technology

收录：CSTPCD;;Scopus;北大核心:【北大核心2011】；CSCD:【CSCD2013_2014】；

基金：国家自然科学基金(20804015)

语种：中文

中文关键词：SBA-15;羟基;聚己内酯;聚氨基己内酯;Zeta电位

外文关键词：SBA-15; hydroxyl; poly（caprolactone）; poly（y-amino-ε caprolactone）; Zeta potential

摘要：利用环氧丙醇对介孔二氧化硅SBA-15的表面进行碳羟基修饰,然后以此为引发剂,异辛酸亚锡为催化剂,分别引发己内酯(CL)及氨基甲酸苄基酯-ε-己内酯((CABCL)单体的开环聚合,成功地制备了杂化材料聚己内酯/SBA-15(PCL/SBA-15)和聚4-氨基甲酸苄基酯己内酯/SBA-15(PCABCL/SBA-15),酸解去除PCABCL/SBA-15的保护基团甲酸苄酯(Cbz)后得到聚氨基己内酯/SBA-15(PACL/SBA 15)。通过X射线衍射仪(XRD)、N_2吸附-脱附实验和热重分析(TGA)等手段研究了材料的结构变化、反应时间和空间位阻效应对接枝量的影响等。结果表明:聚合物的修饰未对介孔结构产生影响;PCL的接枝量可以通过聚合反应时间进行控制;对PACL/SBA-15而言,因CABCL中Cbz的位阻效应导致接枝量较小;Zeta电位分析的结果证明聚氨基己内酯的修饰改变了二氧化硅表面的电荷性质。
Hydroxyl modified SBA 15 （SBA-15-OH） was achieved by the reaction with glycidol. Using Sn（（）ct）2 as catalyst, the ring opening polymerization of ε-caprolactone and γ- （carbamic acid benzyl ester） ε-caprolactone was initiated by SBA-15-OH, and the hybrids poly（caprolactone）/SBA 15 （PCL/SBA-15） and poly γ-（arbamic acid benzyl ester）-~ caprolactone）/SBA-15 （PCABCL/SBA-15） were obtained. After removal of the protective groups （Cbz） by acid, poly（γ-amino-ε caprolactone）/SBA-15 （PACL/SBA 15） was obtained. The structural change and the content of the grafted polymer were analyzed by XRD, nitrogen adsorption-desorption and TGA. The results showed that the polymer modification did not affect the mesoporous structure of hybrids and the grafted amount of PCL could be controlled by reaction time. For PACL/SBA-15, the steric effect of the Cbz groups in CABCL led to the low grafting content in polymerization. Moreover, the Zeta potential results demonstrated that the surface charge property of silica was regulated by the modification of PACL.