英文题名：Effects of annealing temperature on the microstructure, mechanical and tribological properties of CrAlTiN coatings

作者：Huang, Biao[1,2];Zhang, Er-geng[2];Du, Hao-ming[3];Chen, Qiang[2];Liang, Dan-dan[2];An, Qi[1];Zhou, Qiong[2]

机构：[1]East China Univ Sci & Technol, Sch Mech & Power Engn, Shanghai 200237, Peoples R China;[2]Shanghai Inst Technol, Shanghai Engn Res Ctr Phys Vapor Deposit PVD Super, Shanghai 201418, Peoples R China;[3]Shanghai Dianji Univ, Sch Mat Sci & Engn, Shanghai 200240, Peoples R China

年份：2022

卷号：449

外文期刊名：SURFACE & COATINGS TECHNOLOGY

收录：;EI(收录号：20224312994472);WOS:【SCI-EXPANDED(收录号:WOS:000878667600003)】；

基金：This work is supported by the Natural Science Foundation of China (Grant Nos. 51971148) .

语种：英文

外文关键词：Annealing temperature; CrAlTiN coatings; Microstructure; Mechanical properties; Tribological properties

摘要：The microstructure, mechanical properties and tribological properties of CrAlTiN coatings with various atmo-spheric annealing temperature are systematically investigated. The results show that the hardness of the coating decrease with the annealing temperature increasing from room temperature to 800 degrees C, however, the elastic strain resistance H/E value increase firstly and then decrease. The deposited CrAlTiN coating is face-centered cubic structure, (111) and (200) planes show competition growth, while high annealing temperature promotes the growth of (200) planes. The main wear mechanisms of CrAlTiN coating against Si3N4 ball are adhesive and oxidative. The coatings annealed at 400 degrees C has the lowest wear rate and annealed at 800 degrees C peeled off during the friction process. The chromium oxide, aluminium oxide and titanium oxide with lubricating and high hardness adhered on the wear tracks, playing the role of supporting the counterballs, a low COF of the coating is obtained. The coatings annealed above 600 degrees C are more easily to form extensive smooth and dense oxide adhesives, but it takes longer to reach stable wear stage. Thus, the preferred annealing temperature could effectively regulate the microstructure and improve the mechanical and tribological properties of CrAlTiN coating.