英文题名：Experiment and simulation of foaming injection molding of polypropylene/nano-calcium carbonate composites by supercritical carbon dioxide

作者：Xi, Zhenhao[1,2];Chen, Jie[1,2];Liu, Tao[1];Zhao, Ling[1];Turng, Lih-Sheng[2]

机构：[1]E China Univ Sci & Technol, State Key Lab Chem Engn, Shanghai 200237, Peoples R China;[2]Univ Wisconsin, Dept Mech Engn, Madison, WI 53706 USA

会议论文集：6th Global Chinese Symposium of Chemical Engineering

会议日期：JUL 16-19, 2014

会议地点：Pokfulam, PEOPLES R CHINA

语种：英文

外文关键词：Microcellular injection molding; Isotactic polypropylene/nano-calcium carbonate; Cell morphology; Nucleation activation energy; Numerical simulation

摘要：Microcellular injection molding of neat isotactic polypropylene (iPP) and isotactic polypropylene/nano-calcium carbonate composites (iPP/nano-CaCO3) was performed using supercritical carbon dioxide as the physical blowing agent. The influences of filler content and operating conditions on microstructure morphology of iPP and iPP/nano-CaCO3 microcellular samples were studied systematically. The results showed the bubble size of the microcellular samples could be effectively decreased while the cell density increased for iPP/nano-CaCO3 composites, especially at high CO2 concentration and back pressure, low mold temperature and injection speed, and high filler content. Then Moldex 3D was applied to simulate the microcellular injection molding process, with the application of the measured ScCO2 solubility and diffusion data for iPP and iPP/nano-CaCO3 composites respectively. For neat iPP, the simulated bubble size and density distribution in the center section of tensile bars showed a good agreement with the experimental values. However, for iPP/nano(-)CaCO3 composites, the correction factor for nucleation activation energy F and the pre-exponential factor of nucleation rate f(0) were obtained by nonlinear regression on the experimental bubble size and density distribution. The parameters F and f(0) can be used to predict the microcellular injection molding process for iPP/nano-CaCO3 composites by Moldex 3D. (C) 2015 The Chemical Industry and Engineering Society of China, and Chemical Industry Press. All rights reserved.