文献类型：期刊文献

中文题名：改性逆热致相分离法制备亲水性聚醚砜超滤膜及其性能

英文题名：Preparation and Properties of Hydrophilic Polyethersulfone Ultrafiltration Membrane by Modified RTIPS

作者：杨静[1];魏永明[2];贾宇翔[3];束长朋[3];刘敏[1];周权[1]

机构：[1]华东理工大学材料科学与工程学院,上海200237;[2]华东理工大学化工学院,上海200237;[3]上海航天设备制造总厂有限公司上海航天特种环境高分子功能材料工程技术研究中心,上海200245

年份：2023

卷号：39

期号：9

起止页码：81

中文期刊名：高分子材料科学与工程

外文期刊名：Polymer Materials Science & Engineering

收录：CSTPCD;;EI(收录号：20234715075291);Scopus;北大核心:【北大核心2020】；CSCD:【CSCD2023_2024】；

基金：国家自然科学基金面上项目(21978082)。

语种：中文

中文关键词：聚醚砜膜;四元低临界共溶温度体系;改性逆热致相分离法;亲水性

外文关键词：polyether sulfone membrane;quaternary membrane formation system with a low critical solution temperature;modified reverse thermally induced phase separation;hydrophilicity 89

摘要：通过在非低临界共溶温度三元成膜体系聚醚砜(PES)/N,N-二甲基乙酰胺(DMAc)/一缩二乙二醇(DEG)中添加亲水性超支化聚酯(HBPE)成功构建了四元低临界共溶温度(LCST)成膜体系,采用改性逆热致相分离(m-RTIPS)法一步制备了亲水性PES微孔膜。通过扫描电镜、亲水性、渗透性和力学性能实验研究了LCST体系的构建机理和HBPE添加量对膜结构和性能的影响。结果表明,随着HBPE质量比的增加,铸膜液体系的LCST降低;以m-RTIPS法所制得的膜表面开孔率较高、平均孔径较大且可抑制膜断面指状孔的形成并向双连续结构转变,同时膜的渗透性能和力学性能均优于NIPS法所制膜;膜表面的接触角随HBPE质量比的增加而减小,表面膜的亲水性得到改善,抗污染能力增强。
A novel method was presented to construct a quaternary membrane formation system featured a low critical solution temperature(LCST)by incorporating hydroxy terminated hyperbranched polyester(HBPE)into ternary membrane formation system PES/DMAc/DEG which was a non-LCST system,and hydrophilic polyether sulfone(PES)microporous membranes were prepared via modified reverse thermally induced phase separation(m RTIPS)process.The construction mechanism of LCST system and effect of HBPE content on the structure and properties of PES membranes were studied by morphology,hydrophilicity,permeation performance and mechanical properties.The results show that the cloud point decreases as the HBPE concentration increases.SEM images reveal that there are more pores on the top surface and bigger mean pore size when using m-RTIPS process rather than NIPS.In addition,finger-like pores in the cross-section gradually disappear and transfer to bicontinuous structure.When the membranes were prepared via m-RTIPS,the PES membranes show better permeation properties and mechanical properties than the membranes prepared via NIPS process.Furthermore,the water contact angle decreases with the addition of HBPE,which indicates that the hydrophilicity of membrane surface is improved,and the anti fouling property is also enhanced.