文献类型：期刊文献

英文题名：Extrusion foaming of poly(ethylene terephthalate) with carbon dioxide based on rheology analysis

作者：Fan, Chaoyang[1];Wan, Chen[1];Gao, Feng[1];Huang, Chao[1];Xi, Zhenhao[1];Xu, Zhimei[1];Zhao, Ling[1];Liu, Tao[1]

机构：[1]E China Univ Sci & Technol, State Key Lab Chem Engn, Meilong Rd 130,Campus Box 369, Shanghai 200237, Peoples R China

年份：2016

卷号：52

期号：3

起止页码：277

外文期刊名：JOURNAL OF CELLULAR PLASTICS

收录：;EI(收录号：20161802333781);WOS:【SCI-EXPANDED(收录号:WOS:000375007700002)】；

基金：The authors are grateful to the National Programs for High Technology Research and Development of China (863 Project, 2012AA040211) and fundamental research funds for the central universities.

语种：英文

外文关键词：PET; carbon dioxide; extrusion foaming; rheology; viscoelasticity

摘要：Although low density poly(ethylene terephthalate) foams take advantage of the combination of good performances and lightness and have a wide range of engineering applications, extrusion foaming of the poly(ethylene terephthalate) is still faced with many challenges, especially the inadequate rheological characteristics. In this work, the melt strength of four types of poly(ethylene terephthalate) was compared on the basis of the analysis on the dynamic complex viscosity, storage and loss modulus, relaxation spectrum, loss factor and extensional viscosity using rheometer. It was found that the two long chain branching poly(ethylene terephthalates) owned overall higher melt viscosity and greater elasticity than the other two linear ones. Furthermore, only one long chain branching poly(ethylene terephthalate), i.e. PET4, succeeded in the extensional viscosity characterization and showed the phenomenon of strain hardening. Thereafter, PET4 was successfully applied for the extrusion foaming with CO2 as the blowing agent. The effects of the foaming temperature, screw revolution speed, gas input and addition of nucleation agent were carefully investigated on the extrusion foaming and the resulted poly(ethylene terephthalate) foams properties. Under the optimization condition, the extruded poly(ethylene terephthalate) foams were produced with the volume expansion ratio of 9.5, average cell size of 265 mu m, cell density of 4.58 x 10(5) cells/cm(3) and a narrow cell size distribution.