中文题名：天然橡胶/石墨烯纳米复合材料的制备及耐核辐射性能

英文题名：Fabrication of Natural Rubber/Chemically Reduced Graphene Oxide Nanocomposites and Nuclear Radiation Resistant Behavior

作者：刘尧华[1];林宇[1];张栋葛[1];陈春蕾[1];吴国章[1];张衍[1];栾伟玲[2]

机构：[1]华东理工大学材料科学与工程学院,上海市先进聚合物重点实验室,上海200237;[2]华东理工大学机械与动力工程学院,承压系统与安全教育部重点实验室,上海200237

年份：2016

卷号：37

期号：7

起止页码：1402

中文期刊名：高等学校化学学报

外文期刊名：Chemical Journal of Chinese Universities

收录：CSTPCD;;EI(收录号：20163102668273);Scopus;WOS:【SCI-EXPANDED(收录号:WOS:000380076900026)】；北大核心:【北大核心2014】；CSCD:【CSCD2015_2016】；

基金：Supported by the National Basic Research Program of China(No. 2013CB035505) and the National Natural Science Foundation of China (Nos. 51373053, 51503066).

语种：中文

中文关键词：天然橡胶/石墨烯纳米复合材料;耐辐射性;拉伸强度;热稳定性;自由基猝灭剂

外文关键词：Natural rubber/reduced graphene oxide nanocomposite; Radiation resistant behavior; Tensile strength; Thermal stability; Free radical scavenger

摘要：采用乳液共混和原位还原法制备了天然橡胶(NR)/还原氧化石墨烯(RGO)纳米复合材料,研究了γ射线辐照对复合材料力学性能和热稳定性的影响.研究结果表明,RGO以少数几层堆叠片层结构均匀分散于NR基体中.RGO的加入可显著提高NR的力学性能和热稳定性,加入质量分数为0.6%的RGO可使材料拉伸强度由(22±1.4)MPa提升至(25±1.1)MPa,质量损失50%对应的温度(T50)升高6.4℃.经200 k Gy的γ射线辐射后,纯NR的拉伸强度和T50分别下降了75%和4.5℃,而NR/RGO-0.6%复合体系仅分别下降了56%和1.2℃.揭示了RGO提高材料耐辐射性能的机理,由于RGO可捕捉猝灭因辐射产生的自由基,从而减弱了辐射老化降解和交联反应的发生.
Natural rubber（ NR） / chemically reduced graphene oxide（ RGO） nanocomposites were fabricated by latex mixing plus in situ reduction process. The transmission electron microscopy morphology shows that uniform dispersion of RGO with a few layers of stacked lamellar structure can be observed in the nanocomposites. The effect of γ irradiation on the mechanical property and thermal stability of NR matrix by the incorporation of RGO was mainly investigated in detail. Compared to pure NR,the tensile strength increases from（ 22 ±1. 4） MPa to（ 25 ±1. 1） MPa and the thermal decomposition temperature of 50% mass loss（ T50） is increased by 6. 4 ℃ for NR / RGO nanocomposites by the addition of 0. 6% RGO before irradiation. After γirradiation dose of 200 k Gy,the tensile strength and T50 of pure NR are decreased by 75% and 4. 5 ℃,respectively. However,those of NR / RGO-0. 6% nanocomposites are decreased only by 56% and 1. 2 ℃,respectively. The radiation resistant mechanism of NR / RGO nanocomposites was also interpreted by electron paramagnetic resonance measurements. The results reveal that RGO can act as free radical scavenger,and the introduction of RGO to NR matrix exhibits much less amount of free radicals.